微波对高链玉米淀粉颗粒抗消化性能的影响

食品科学 ›› 2007, Vol. 28 ›› Issue (10): 105-108.

微波对高链玉米淀粉颗粒抗消化性能的影响

李晓玺, 陈玲, 邹芳建, 穆燕, 李琳

华南理工大学轻化工研究所；华南理工大学轻化工研究所广东广州510640；广东广州510640；

出版日期:2007-10-15 发布日期:2011-11-22

Effect of Microwave on Digestion Resistibility of High Amylose Maize Starch Granule

LI Xiao-Xi, CHEN Ling, ZOU Fang-Jian, MU Yan, LI Lin

Light Industry and Chemical Engineering Research Institute, South China University of Technology, Guangzhou 510640, China

Online:2007-10-15 Published:2011-11-22

摘要/Abstract

摘要： 高链玉米淀粉颗粒通过微波改性,调节不同的水分质量分数、微波温度、微波时间和微波功率可以改变淀粉颗粒的抗消化性能。采用扫描电镜和生物体外(invitro)降解方法,对不同微波作用条件下的高链玉米淀粉的颗粒形貌和抗消化性能进行了研究。结果表明,高链玉米淀粉经微波改性后,颗粒形貌发生改变,表面出现凹凸、小孔,当抗消化淀粉质量分数达到22.0%时,大部分淀粉颗粒已经发生破损、崩裂。在微波场中,水分质量分数和微波温度对高链玉米淀粉抗消化性能的影响较大,而微波功率和时间对其影响较小。

关键词: 微波改性, 高链玉米淀粉, 颗粒形貌, 抗消化性能

Abstract: The high amylose maize starch granules were modified by the microwave and their digestion resistibility was changed under different moisture mass percents, microwave temperatures, treatment time and powers. The granule appearance and digestion resistibility of native and microwave modified high amylose starch granules under different microwave conditions were investigated by SEM and in in vitro digestion model. It was found that the microwave modified starch granule surface became roughness and most of them were damaged to some little fragment when the resistant starch content reached 22.0%. The results showed that under the microwave filed the moisture mass percent and microwave temperature had significant effects on the high amylase maize starch digestion resistibility but the microwave power and time had little effect.

Key words: microwave modification, high amylose maize starch, granule appearance, digestion resistibility

李晓玺, 陈玲, 邹芳建, 穆燕, 李琳. 微波对高链玉米淀粉颗粒抗消化性能的影响[J]. 食品科学, 2007, 28(10): 105-108.

LI Xiao-Xi, CHEN Ling, ZOU Fang-Jian, MU Yan, LI Lin. Effect of Microwave on Digestion Resistibility of High Amylose Maize Starch Granule[J]. FOOD SCIENCE, 2007, 28(10): 105-108.

[1]	莫芳，徐晓萍，陶晓奇，陈厚荣，张甫生. 高静压对木薯淀粉理化特性及结构的影响[J]. 食品科学, 2018, 39(17): 109-115.
[2]	李坚斌，陈小云，张帆，陆登俊，廖文敏. 葡甘露聚糖微波法磷酸酯化改性研究[J]. 食品科学, 2015, 36(8): 19-23.
[3]	张晓，任清. 压热酶脱支重结晶法制备甜荞抗性淀粉的工艺优化及颗粒形貌[J]. 食品科学, 2013, 34(8): 64-69.
[4]	韩春然，姚珊珊，许鑫. 奶白花芸豆淀粉颗粒结构及理化特性研究[J]. 食品科学, 2012, 33(3): 63-67.
[5]	范蓓，马静，李淑荣，李庆鹏，王锋，周洪杰，哈益明. 60Co-γ辐射对马铃薯淀粉特性的影响[J]. 食品科学, 2011, 32(21): 17-19.
[6]	赵娜，杨超，田斌强，孙智达*,谢笔钧. 加热时间对大米淀粉特性及抗性淀粉含量的影响[J]. 食品科学, 2010, 31(15): 34-38.
[7]	徐忠, 缪铭, 刘明丽, 张海华. 玉米多孔淀粉颗粒结构及性质的研究[J]. 食品科学, 2006, 27(10): 128-132.